Recent insights in synthesis and energy storage applications of porous carbon derived from biomass waste: A review

In the last few decades, global warming, environmental pollution, and an energy shortage of fossil fuel may cause a severe economic crisis and health threats. Storage, conversion, and application of regenerable and dispersive energy would be a promising solution to release this crisis. The development of porous carbon materials from regenerated biomass are competent methods to store energy with high performance and limited environmental damages. In this regard, bio-carbon with abundant surface functional groups and an easily tunable three-dimensional porous structure may be a potential candidate as a sustainable and green carbon material. Up to now, although some literature has screened the biomass source, reaction temperature, and activator dosage during thermochemical synthesis, a comprehensive evaluation and a detailed discussion of the relationship between raw materials, preparation methods, and the structural and chemical properties of carbon materials are still lacking. Hence, in this review, we first assess the recent advancements in carbonization and activation process of biomass with different compositions and the activity performance in various energy storage applications including supercapacitors, lithium-ion batteries, and hydrogen storage, highlighting the mechanisms and open questions in current energy society. After that, the connections between preparation methods and porous carbon properties including specific surface area, pore volume, and surface chemistry are reviewed in detail. Importantly, we discuss the relationship between the pore structure of prepared porous carbon with surface functional groups, and the energy storage performance in various energy storage fields for different biomass sources and thermal conversion methods. Finally, the conclusion and prospective are concluded to give an outlook for the development of biomass carbon materials, and energy storage applications technologies. This review demonstrates significant potentials for energy applications of biomass materials, and it is expected to inspire new discoveries to promote practical applications of biomass materials in more energy storage and conversion fields.     

The influence of carbon atom distribution in precursors with 1:1 carbon to silicon atoms ratio on structure and thermal evolution of obtained silicon oxycarbide based materials

In this work, a number of precursors with 1:1 silicon to carbon atoms ratio and various carbon atom distributions were synthesized and pyrolyzed in order to obtain silicon oxycarbide based materials. The different carbon atom distributions were obtained using both simple monomers with only one silicon atom, as well as large monomers containing either four or sixteen silicon atoms with predefined carbon atom positions. The silicon oxycarbide based materials were investigated using IR, XRD, ²⁹Si MAS NMR and elemental analysis after annealing at various temperatures, as well as TG. The research shows that carbon atom distribution has great impact on the structure of final material and can be used to tailor the material for its projected uses.     

Effect of aluminium acetyl acetonate on the hydrogen and nitrogen permeation of carbon molecular sieves membranes

With a growing interest in hydrogen as energy carrier, the efficient purification of hydrogen from gaseous mixtures is very important. This paper addresses the separation of hydrogen using Carbon Molecular Sieves Membranes (CMSM), which show an attractive combination of high permeability, selectivity and stability. Supported CMSM containing various amounts of aluminium have been prepared from novolac and aluminium acetyl acetonate (Al(acac)₃) as carbon and alumina precursors. The thickness of the CMSM layers depend on the content of Al(acac)₃ in the dipping solution, which also has influence in the pore size and pore size distribution of the membranes. The permeation properties of the membranes against the Al content in the membrane follows a volcano shape, where the membrane containing 4 wt (%) of Al(acac)₃ has the best properties and was stable during 720 h for hydrogen at 150 °C and 6 bar pressure difference. All the CMSM have permeation properties well above the Robeson Upper limit.     

Carbon corrosion mechanism on nitrogen-doped carbon support — A density functional theory study

In this work, density functional theory (DFT) calculations were used to investigate the mechanism of carbon corrosion on nitrogen-doped carbon support. Free energy diagrams were generated based on three proposed reaction pathways to evaluate corrosion mechanisms. The most energetically preferred mechanism on nitrogen-doped carbon was determined. The results show that the step of water dissociation to form ^#OH was the rate-determining step for gra-G-1N (graphene doped with graphitic N) and pyrr-G-1N (graphene doped with pyrrolic N). As for graphene doped with pyridinic N, the step of C^#OC^#O formation was critical. It was found that the control of nitrogen concentration was necessary for precisely designing optimized carbon materials. Abundance of nitrogen moieties aggravated the carbon corrosion. When the high potential was applied, specific types of graphitic N and pyridinic N were found to be favorable carbon modifications to improve carbon corrosion resistance. Moreover, the solvent effect was also investigated. The results provide theoretical insights and design guidelines to improve corrosion resistance in carbon support through material modification by inhibiting the adsorption of surface oxides (OH, O, and OOH).     

多晶硅表面金属催化化学腐蚀法制绒研究现状

在多晶硅太阳能电池的生产过程中, 金刚线切割技术(Diamond wire sawn, DWS)具有切割速度快、精度高、原材料损耗少等优点, 受到了广泛关注。金刚线切割多晶硅表面形成的损伤层较浅, 与传统的酸腐蚀制绒技术无法匹配, 金属催化化学腐蚀法应运而生。金属催化化学腐蚀法制绒具有操作简单、结构可控且易形成高深宽比的绒面等优点, 具有广阔的应用前景。本文总结了不同类型的金属催化剂在制绒过程中的腐蚀机理及其形成的绒面结构, 深入分析和讨论了具有代表性的银、铜的单一及复合催化腐蚀过程及绒面结构和电池片性能。最后对金刚线切割多晶硅片表面的金属催化化学腐蚀法存在的问题进行了分析, 并展望了未来的研究方向。     

异种铁素体耐热钢接头界面组织及其影响

综述了铁素体与铁素体异种金属焊缝（dissimilar metal welds，DMWs）接头界面组织及其影响。结果表明，在焊后热处理或运行温度下的铁素体钢DMWs接头的不均匀界面组织中，通常会形成脱碳层和增碳层。在铁素体钢DMWs焊接接头界面组织影响因素中，焊缝金属的化学成分有重要影响；焊后热处理规范（温度和时间）、工作温度下运行时间的影响较为突出；焊接工艺参数的影响亦不可忽略。异种钢接头界面处近缝区裂纹的产生，以及接头的蠕变强度随Larson Miller 参数增大而下降等不利影响，均为异种钢界面碳迁移行为所导致。焊缝成分控制法是接头界面组织控制或改善的必要条件，而脱碳层部位转移法能有效防止裂纹发生，亦是接头安全运行的重要工艺措施之一。     

Phase composition,microstructure, and properties of Al4O4C–(Al2OC)1-x(AlN)x –Zr2Al3C4–Al2O3 refractories prepared at high temperatures in nitrogen

The novel Al₄O₄C–(Al₂OC)_1-x(AlN)_x–Zr₂Al₃C₄–Al₂O₃ refractories with ultra-low carbon content have been successfully prepared by constructing the core-shell structure of aluminum at 1300–1700°C in nitrogen. The phase composition, microstructure, and properties of the novel refractories are deeply investigated. The cracking temperature on the core-shell structure of aluminum is further explored and the reaction mechanism of Zr₂Al₃C₄ has also added explanation. The results show that the novel refractories have excellent physical properties and cannot be corroded by molten iron. There exist two different Al₂OC solid solutions in the novel refractories, Al₂OC-rich (Al₂OC)_1-x(AlN)_x and AlN-rich (Al₂OC)_1-x(AlN)_x. The temperatures affect their relative content. When temperatures are less than 1600°C, the relative content of Al₂OC-rich (Al₂OC)_1-x(AlN)_x is more than that of AlN-rich (Al₂OC)_1-x(AlN)_x. When temperatures are above 1700°C, the relative content of AlN-rich (Al₂OC)_1-x(AlN)_x is more than that of Al₂OC-rich (Al₂OC)_1-x(AlN)_x. The core-shell structure of aluminum fully ruptures at about 1200°C. Zr₂Al₃C₄ begins to form at about 1000°C and generates in large at 1200°C.     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

Potential influence of microorganisms on the corrosion of carbon steel in the French high- and intermediate-level long-lived radioactive waste disposal context

In the context of the high-level radioactive waste disposal CIGEO, the corrosion rate due to microbially influenced corrosion (MIC) has to be evaluated. In France, it is envisaged to dispose of high- and intermediate-level long-lived radioactive waste at a depth of 500 m in a deep geological disposal, drilled in the Callovo-Oxfordian claystone (Cox) formation. To do so, a carbon steel casing will be inserted inside disposal cells, which are horizontal tunnels drilled in the Cox. A specific cement grout will be injected between the carbon steel casing and the claystone. A study was conducted to evaluate the possibility of MIC on carbon steel in the foreseeable high radioactive waste disposal. The corrosiveness of various environments was investigated at 50°C and 80°C with or without microorganisms enriched from samples of Andra's underground research laboratory. The monitoring of corrosion during the experiments was ensured using gravimetric method and real-time corrosion monitoring using sensors based on the measurements of the electrical resistance. The corrosion data were completed with microbiological analyses including cultural and molecular characterizations.